Product Description
POLYESTER ACP
Polyester Aluminum Composite Panel offers a wide-range of standard or custom colors incorporating the reliable polyester lacquer system for creative possibilities of applications. With durable, vivid colors and the best quality of the polyethylene core Polyester Aluminium Composite Panel is recommended for interior decoration and sign board.
Constitution Structure:
Standard Products:
For Exterior: 1220X2440X4MM, al: 0.3mm,0.4mm,0.50MM, PVDF
For Interior: 1220X2440X3MM, al: 0.10mm,0.12MM,0.18MM.0.21MM PE
Products Available:
Thickness: 2mm, 3mm, 4mm, 5mm, 6mm, 7mm, 8mm
Length: can be customized
Width: 800mm~1570mm
Aluminum thickness: 0.12mm, 0.18MM ,0.21mm, 0.30mm, 0.40mm, 0.50mm
Coating: Polyester coating, Fluorocarbon coating.
Scope of Application: Internal and external decoration for all kinds of buildings, airports, ceilings, tunnels, billboards, doors, furniture, car bodies, ships, etc.
Cutting: Cut with a saw, cutter, or trimmer.
Cleaning and Maintenance: Clean with water or neutral cleaner, using a soft cloth. Do not use force. Do not use a knife or other sharp object.
Technical data:
Based on 1220*2440mm, 3mm(0.2+0.2) aluminium skins.
| Testing items | Result | Testing items | Result | Testing items | Result | |
| Appearance quality |
Vestige | Indistinct | Weight | t4 mm=5.7kg/m | Finish coating thickness | 30+-5um |
| Coating amit | No | Outdoor temperature | NO abnormity | Gloss talerance | 4.3 (gloss56.8) | |
| Ripples | No | Thermal expansion | 1.59*10-3.0 c-1 | Pencil hardness | 3H | |
| Flaw | No | Deflection temperature | 105 c | Toughness(T-bend) | 2T no rift | |
| Aberation | No | Thermal conductivity | 0.102 kcal/m.hrc | Coating achesive farce | Class 1 (4B) | |
| Scratch | No | Flexural rigidity | 14.0-103 | Impact resistance (50kg.cm) |
no depainting. no crack |
|
| Aberation | Indistinct | penetrating resistance | 9.0KN | Grinding resistance | 7.4l/um | |
| 180° peel strength | 11.7N/mm | Mortar resistance | 24 Hrspat test exceed | |||
| Dimensians deviaticn |
Length | 0~+0.4mm | Acoustic insulation | 25 dB | Humidity resistance | 3000hr no blister |
| Width | 0~+0.6mm | Bending elastic modulus | 2.8*10MPa | Bailing-water resistance | No change | |
| Thickness | -0.02~0mm | Shearing resistance | 28.6MPa | Salt-spray resistance | 3000hr no blister | |
| Diagonals windage |
1.7mm | Fire propagation | Qualified | Acidresistance | No change | |
| Edge unstraightness |
0.4mm/m | Wind-pressure resistance | Passed | Alkali resistance | Passed | |
| Warpage | 2.0mm/m | Properites against water | Passed | Salvent resistance | Passed | |
| Properites against air | Passed | Color retention | E<5 | |||
| Bending strenght | 112MPa | Chalk resistance | Max value 8 unit | |||
| Minimum bending redius | ~300MM | Gloss retention | 90% | |||
Conclusion:
The test results meet the index requirements of quality products of GB/T 17748-1999 and the products samples are as quality products in the industry of aluminum composite panel in China